Part Number WS 1.3505
Technical Data Sheet
CCR-1150 is a ball bearing steel which is manufactured in Rod, Bar and coil.
| Chemical Composition Limits | |||||||
| Weight % | C | Si | Mn | P | S | Cr | Fe |
| CCR-1150 | 0.95-1.10 | 0.15-0.35 | 0.25-0.45 | 0.03 max | 0.025 max | 1.35-1.65 | Rem |
| Other Chemically similar Specifications | |||||||
| Weight % | C | Si | Mn | P | S | Cr | Fe |
| WS 1.3505 | 0.95-1.10 | 0.15-0.35 | 0.25-0.45 | 0.03 max | 0.025 max | 1.35-1.65 | Rem |
| EN 100 Cr 6 | 0.95-1.10 | 0.15-0.35 | 0.25-0.45 | 0.03 max | 0.025 max | 1.35-1.65 | Rem |
| AISI 52100 | 0.95-1.10 | 0.15-0.35 | 0.25-0.45 | 0.03 max | 0.025 max | 1.35-1.65 | Rem |
| AFNOR 100 C 6 | 0.95-1.10 | 0.15-0.35 | 0.25-0.45 | 0.03 max | 0.025 max | 1.35-1.65 | Rem |
For all stock and size availability contact Sales.
(WS 1.3505 Ball Bearing Steel, AISI 52100 Ball Bearing Steel)
Available in:
coils: Cold drawn + polished: 10-35kg/coil
Bars: Ø0-2.99mm: cold drawn and polished
Bars: Ø 3.00-19mm: cold drawn, ground and polished
Bar Lengths: 2m (3m) Surface finish N5-N6
Tolerance to:
Diameter : ISO h9 and h8
Out of Roundness/ eccentricity: 1/2 the diam. tolerance.
Tolerance in length: +/-30mm
Heat treatment
Hardening :830-870 ºC quenching in oil
:800-830 ºC quenching in water
:730-760 ºC soft annealing
:870-900 ºC normalising
Obtainable Hardness 58-66 HRC
Standard Stock Sizes:
Ø 1-40mm with steps of sometimes 0.50mm special sizes and narrow tolerances available on request
Cutting rate
25-40m/min (approximate value, depending on the lubrication oil, the cutting tools, and shape of parts.)
Return to Main Precision Ground Material
Customer Reviews - What Customers Say About Us!
| CLICK HERE TO VIEW OUR BROCHURE |
Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.