Aircraft Stainless Steel Jethete M152 (BS S151/ S159)


Technical Data Sheet

Jethete M152 is a creep and corrosion resistant, hardened and tempered steel with a usual upper temperature limit of 560°C. It combines very good toughness and creep rupture properties making it an excellent alloy for use in highly stressed turbine blades, discs, screws, bolts and rings. Jethete M152 is supplied by Aircraft Materials in both bar form, to British Standards BS S151 and BS S159 and in sheet form to Rolls Royce specifications MSRR 6504 and MSRR 6514. It can also be supplied in mill productions to the US Aerospace specification AMS 5719.

Chemical Composition Limits
Weight% C Si Mn P+S max Cr Mo Ni N V
Jethete M152 0.08-0.13 0.35 max 0.50-0.90 P 0.030
S 0.025
11-12.5 1.50-2.0 2-3 0.02-0.04 0.25-0.40

Jethete M152 is supplied in various different types of heat treatment depending on the specification required. The standard heat treatments for Jethete M152 are as follows:

BS S151 (MSRR 6503)
Softening: 670-720° C for 6 hours followed by air cool - Designated BS S151A
Harden: 1050° C (+/-10) followed by air cool
Temper: 650° C (+/-5) followed by air cool - Designated BS S151D

BS S159
Softening: 680-700° C for 2 hours min followed by air cool - Designated BS S159A
Harden: 1050° C (+/-10) for 30 minutes min followed by air cool
Temper: 560-590° C for 3 hours min followed by air cool - Designated BS S159D
Stress Relieve: Can be performed on hardened and tempered bars if a cold rolling operation has taken place, by holding at 30° C lower than the tempering temperature.

AMS 5719
Anneal: 691° C (+/-11) for 6 hours min followed by air cool
Harden:1052° C (+/-) for 30 mins followed by oil quench
1st Temper: 560-590° C for 1 hour min followed by air cool
2nd Temper: 538-560° C for 3 hours min followed by air cool

Mechanical Properties Comparison

 

Grade Treatment Tensile Strength
Mpa
Yield Strength
Mpa
Elongation % Hardness HB Ruling Section
S151A
S151D
Softened
Finally Heat Treated

930-1130

780

14
311max
286-311
-
150mm
S159A
S159D
Softened
Finally Heat Treated

1100-1300

900

8
311 max
321-388
50mm
AMS 5719
AMS 5719
Annealed
Hardened & Double Templerd

1069 min

896

12
311
341-375
-
-

Availability
Jethete M152 is available in bar and sheet. For all other stock availability contact Sales.

Specifications
Jethete M152
BS S151
BS S159
MSRR 6503
MSRR 6504 - Jethete M152 sheet
MSRR 6514 - Jethete M 152 sheet
AMS 5719
DTD 5066
WS 1.4933
WS 1.4938
WS 1.4939
Z12CNDV12
AECMA FE-PM37
UNS S64152

Customer Reviews - What Customers Say About Us!

"Just wanted to say thanks for your efforts and updates"
"I always try you as you often keep stock that can't be found elsewhere"
"Prompt answer & knowledge of available material, timescale & price within a good time"
"Packaging is superb"
"Thank you for your quick response"
  CLICK HERE TO VIEW OUR BROCHURE  

Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.