Cobalt Alloy 25/ Haynes © Alloy 25/ Udimet L605/ Alloy L-605
Technical Data Sheet
| Chemical Composition Limits | ||||||||||
| Weight% | C | P | Si | Ni | W | Mn | S | Cr | Co | Fe |
| Alloy L-605 | 0.05 - 0.15 | 0.040 max | 0.40 max | 9.0 - 11.0 | 14.0 - 16.0 | 1.0 - 2.0 | 0.030 max | 19.0 - 21.0 | Bal | 3.0 max |
Alloy Alloy L-605 (Haynes © Alloy 25) is a non-magnetic chromium, nickel, tungsten, cobalt alloy. L-605 has excellent high temperature strength and good oxidation resistance to 2000ºF (1093ºC). L-605 is used in gas turbines rotors, combustion chambers, various industrial furnace applications and in the medical industry in heart valves.
Typical Mechanical Properties
| Material | Condition | Diameter or Thickness mm |
Tensile Strength Mpa |
0.2% Offset Yield Strength Mpa | Elongation (%) (x4D) | Reduction of Area % |
| Alloy L-605 Bar Alloy 25 |
Annealed | >1.6mm | 917 | 476 | 41 | 33 |
| Alloy L-605 Bar Alloy 25 |
Cold Worked 30% | 1.6-9.5 mm | 1345 | 1000 | 16 | 18 |
Availability
Alloy L-605 (Haynes © Alloy 25) is available in Bar (Rounds), Rod, Wire, Sheet, Strip, Forging Stock, Foil, Welding Wire, Billet and L- 605 Vac Melt Bar. For all stock availability contact Sales.
Specifications
UNS R30605
AMS 5759F Bar and Forging Stock
ASTM F90 Bar and Wire (All implant quality)
AMS 5507 Sheet Strip and Plate
AMS 5796 Welding Wire
AMS 5797 (UNS W73605) Welding Rod
Haynes © Alloy 25